HSS tool steel supplier hot rolled and forged bar AISI M2 DIN 1.3343
AISI M2 M35 T1 (DIN 1.3343 1.3243 1.3355)steel( Hot rolled steel bar) product is our company the most outstanding advantage flagship product using a variety of detection means To ensure the good quality to adopt the latest production technology and equipment Make the production cycle shorten order quantity in the 1000 kg or more to ensure rapid delivery of the goods in the 15 to 20 days
Provide samples, but need to pay the samples fees, 100RMB/Kg.
Packaging & Shipping
package for bars:
the bars will be oiled for rust protection, - one dia should be packed in one bundle by the steel strip; bundles should be oiled and turned into the PE film then packed in wooden boxes for easy loading.
W18 high speed steel
Hss can be used for making cold working mold steel, the hardness main 57HRC-58 HRC, and 52-53 HRC separately under 500°C-600°C. It has good machinability for most of materials.
W18 hss material used for the die steel which requires high hardness, higher compressive strength and wear resisting property, bear higher load, and process hard material, such as overload punch, cold extrusion die steel,high speed heat-resisting and wear-resisting cutting tools, high-temperature bearing and roller ect, has higher hardness, high strength, high crushing resistance, higher wear- resistance and high thermal stability characteristics.
china forged tool steel metal products w18 bar
W18Cr4V is tungsten high speed tool steel, high hardness, red hardness and high temperature strength at 500 °C and 600 °C, respectively, while still maintaining the hardness HRC57-58, HRC52-53, in addition, also has good high temperature strength and wear resistance, a wide temperature range of heat treatment, quenching easily overheat, easy grinding, thermal processing and heat treatment process is not easy oxidation and decarbonization. Usually the material to be processed for a good cutting performance.
Carbide of the steel, high-temperature plasticity than molybdenum high speed tool steel is poor. W18Cr4V cast was bone-like tissue including carbide and martensite or flake troostite alternating ledeburite and black organizations (δ segregation) and white tissue (martensite and retained austenite) . Cast microstructure and chemical composition of high-speed steel is particularly uneven, but does not alter the heat treatment, which must be pressure processing, the coarse eutectic carbides break and evenly distributed, and then use in the manufacture of various cutting tools and mold.
WHY US &CONTACT US
1) Honest: we will strictly adhere to the contract, you will get the exact quality and quantity
from us. We never receive any complain from the clients for the quantity and weight. 2) Competitive price with shipment in time. 3) Strictly control on the quality. 4) More than 16 years experience in the export. 5) Best service after sale: We will be responsible for any disputes and problems occured after
shipment, we assure you that we will be responsible to the end once our service starts.