To meet end users further processing needs, the material what we provided is without heat-treatment.
Our hss materials sold to foreign and domestic market. We have own plant and have reliable professional supplie package for bars: the bars will be oiled for rust protection, - one dia should be packed in one bundle by the steel strip; bundles should be oiled and turned into the PE film then packed in wooden boxes for easy loading.
Tungsten molybdenum high speed steel M2 HSS AISI M2 has a series of advantages, like small carbide and well distributed, higher wear-resistance, and lower cost. the hardness main 57HRC-58 HRC, and 52-53 HRC separately under 500°C-600°C. Bending strength can be 4700MPa, the toughness and thermoplasticity can be improved 50% compare with W18Cr4V, can be used as making different of tools. like drills, screw tap, miller cutter, reamer, knife ect, can be meet normal material request.
Our Services Provide samples, but need to pay the samples fees, 100RMB/Kg.
M2 is widely used in applications requiring a high degree of toughness; grindability, good wear resistance and high hardness.
-Lathe Tools; Planer Tool;
-Drills; Taps; Reamers; Broaches;
-Milling Cutters; Thread Cutters; End Mills;
-Blanking Dies; Gear Cutter; Router Bits.
-Preheat slowly to 1600 F until piece is thoroughly heated through, then increase heat to 1950 F -2050 F.
-DO NOT hot work M2 below 1700 F.
- After forging, allow M2 to cool slowly, packed in lime or other insulating material.( For large forgings, let soak in large furnace at 1450 F, then cool in furnace.)
-Anneal as soon as possible.
-Surface protection-Anneal in controlld atmosphere furnace or pack in an inert material. -Slowly heat M2 to 1550-1600, cool slowly at a rate of 20 F/ hr until furnace is black. Shut down furnace, allow to cool normally, annealed hardness range is 200-240 Brinell.
Temperature 1100-1290 F. Rough machine after stress relieving. Hold tool for 2 hours after reaching full temperature. Cool in furnace to 930 F and then air-cool.
Single-edge cutting tools: 2175-2225 F ( salt bath) 2200 F -2250 F( furnace)
Roating multi-edge cutting tools: 2150 F -2250 F
Punches, dies, etc: 1920-2100 F.
-Temper immediately when piece reaches 150 F or when comfortably hand-held. -Tempering temperature should be in the range of 1250 F-1100 F. -Heat slowly to temperature, hold tools at heat for 2 hours before air cooling. -For best toughness, after tool has cooled, retemper for 2 additional hours at slightly lower temperature.
Packaging & Shipping
Delivery time: Normally is 45 days or by negotation
Packing: First with waterproof wrap, and then in wooden case.
(We accept the customized packing by negotation)
Shipping: According to the sales contract.
1 Q:Do you accept the sample order? A: Yes, we accept the sample order. If you order the small piece in stock, it is free.
But we do not pay for the freight cost. 2Q: How long is your delivery time? A: Usually 45 to 60 days after your down payment, it also according to the material requirement and the quantity you ordered. 3 Q: What is your terms of payment. A: Payment less or equal 10000USD,100% T/T in advance. Payment more than 1000USD, 30% T/T in advance, balance before shippment. Also accept the L/C at sight. 5.Q:What is your working time? A:Monday-Friday : 8:00AM-17:00PM (Beijing time, GMT+08.00) While by whatsapp you can contact me anytime if I am awake up